- Easy to apply due to the self adhering ability of the film.
- Easy to apply and remove without residual adhesive.
|
| Type |
Base Film |
Liner |
HAZE |
Total Light Transmittance |
Surface Resistivity |
Features |
| 50SQ |
50µm PET |
25µm PET |
1.2 |
92.7 |
1.21×1010 |
Re-Adherable,
Anti-Static |
| 50SQD |
50µm PET |
50µm PET |
|
 |
Typical sample test results. Not gurranteed. |
|
| |
| Object |
Prosave SQ |
| PET |
Acrylic Board |
Glass |
| 23°C/50%RH |
0.01 N / 25mm |
0.01 N / 25mm |
0.02 N / 25mm |
| 60°C/90%RH |
0.01 N / 25mm |
0.02 N / 25mm |
0.05 N / 25mm |
| 80°C |
0.01 N / 25mm |
0.01 N / 25mm |
0.05 N / 25mm |
| -20°C |
0.01 N / 25mm |
0.01 N / 25mm |
0.02 N / 25mm
|
|
|
Peel from Prosave side at 300m/min, 180°angle after 250hours. |
|
Typical sample test results. Not gurranteed. |
|
| |
| Object |
Prosave SQ |
| PET |
Acrylic Board |
Glass |
| 23°C/50%RH |
O |
O |
O |
| 60°C/90%RH |
O |
O |
O |
| 80°C |
O |
O |
O |
| -20°C |
O |
O |
O |
|
| O = Good |
|
Visual Inspection after 250hours |
|
Typical sample test results. Not gurranteed. |
|
| |
| |
Dipping Prosave SQ applied with PET |
Dipping Prosave SQ Only |
| Prosave SQ |
Other Brand |
Prosave SQ |
Other Brand |
| 5min |
1hr |
5min |
1hr |
5min |
1hr |
5min |
1hr |
| 10% HCI |
O |
O |
O |
O |
O |
O |
O |
O |
| 5% NaOH |
O |
O |
O |
O |
O |
O |
O |
O |
| Ethanol |
O |
O |
O |
O |
O |
O |
× |
× |
| Ethyl Acetate |
O |
O |
Δ |
× |
O |
O |
× |
× |
| Hexane |
O |
O |
O |
O |
O |
O |
O |
O |
| MEK |
O |
O |
Δ |
× |
O |
O |
× |
× |
| Toluene |
O |
Δ |
× |
× |
O |
Δ |
× |
× |
| Benzine |
O |
O |
O |
O |
O |
O |
O |
O |
| Water |
O |
O |
O |
O |
O |
O |
O |
O |
|
| O = No Degradation |
| Δ = Minor Degradation on the edges |
| × = Adhesive De-lamination |
|
| |
|
|
|